Description
IOTA M6060K A/B is post cured free liquid silicone rubber with high bite force.
Features
Two components, 1:1 mixture ratio
Excellent mold release
VOC is less than 0.5%
Rapid heat curing
Excellent mechanical properties
Meet the requirements of BfR、FDA and ROHS
Application
Baby care
Food contact
Sealing ring
Other injection products, etc.
Curing
Temperature |
Curing time,2mm thickness |
130℃ |
90 S |
150℃ |
45 S |
NOTES
IOTA M6060K A/B a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
2. Only same batch of components A and B could be mixed together.
3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.
Technical data
Properties |
Test method |
Value |
Uncured products |
||
Component A |
|
|
Color |
|
transparent |
Density (23℃) |
|
1.12 g/cm3 |
Viscosity (23℃,10S-1) |
ISO3219 |
350 Pa.s |
Component B |
|
|
Color |
|
transparent |
Density (23℃) |
|
1.12 g/cm3 |
Viscosity (23℃,10S-1 ) |
ISO3219 |
300 Pa.s |
Technical data(A/B mixed) |
|
|
Mixture ratio(weight) |
A:B |
1:1 |
Viscosity(23℃,10S-1) |
ISO3219 |
350 Pa.s |
Curing time |
|
See curing conditions |
Technical data(cured) |
(125±2℃,after vulcanizing 5min) |
|
Color |
|
transparent |
Density (23℃) |
ISO2781 |
1.12 g/cm3 |
Hardness |
DIN 53505 |
60 |
Tensile strength |
DIN 53504 |
9 Mpa |
Elongation |
DIN 53504 |
450% |
Tear strength |
ASTMD 624B |
38 KN/m |
Packaging & storage
A component 200 Kg/drum,B component 200 Kg/dum.
Store under 23℃ to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.