Description
IOTA M6030 A/B is a liquid silicone rubber free of post cured.
Features:
Two component, 1:1 mixing ratio
Excellent mold release
VOC < 0.5%
Rapid heat curing
Excellent mechanical properties
Meet standard of BFR, FDA and RoHS
Application:
Baby care
Food contact
Sealing ring
Other injection products, etc
Curing condition
Temperature |
Curing time:2mm thickness |
130℃ |
90 S |
150℃ |
45 S |
NOTES
1.IOTA M6030 A/B a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
2. Only same batch of components A and B could be mixed together.
3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.
Packing and storage
Component A:200kg/drum, component B: 200kg/drum
Store under 23℃ to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.
Technical index:
Properties |
Test method |
Value |
Uncured |
|
|
Component A |
|
|
Color |
|
Transparent |
Density at 23℃ |
|
1.11 g/cm3 |
Viscosity 23℃,10S-1 |
ISO3219 |
280 Pa.s |
Component B |
|
|
Color |
|
Transparent |
Density at 23℃ |
|
1.11 g/cm3 |
Viscosity 23℃,10S-1 |
ISO3219 |
250 Pa.s |
Technical data(A/B mixed) |
|
|
Mix ratio(weight) |
A:B |
1:1 |
Viscosity 23℃,10S-1 |
ISO3219 |
280 Pa.s |
Curing time |
|
See curing conditions |
Technical data(cured) |
125±2℃*300 S |
|
Color |
|
Transparent |
Density 23℃ |
ISO2781 |
1.11g/cm3 |
Hardness |
DIN 53505 |
30 |
Tensile strength |
DIN 53504 |
7.0 Mpa |
Elongation at break |
DIN 53504 |
600% |