Description
IOTA M4335A/B is a low viscosity liquid silicone rubber with good adhesion to fabrics.
Advantages:
Two component, 10:1 mixing ratio
Excellent liquidity
Good adhesion to fabrics
Rapid heat curing
Excellent mechanical properties
Application:
Silk screen printing
Copper plate transfer printing
Silicone printing
Fingerprint printing, etc
Curing condition
Temperature |
Curing time, 1cm thickness |
125°C |
200s |
NOTES
1. IOTA M4335 A/B is a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
2. Only same batch of components A and B could be mixed together
3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.
Packing and storage
Component A: 20kg/drum, component B: 2kg/drum
Store at room temperature under 23 ℃ to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.
Technical index:
Properties |
Test method |
Value |
Uncured |
|
|
Component A |
|
|
Color |
|
Translucent |
Density 23℃ |
|
1.08 g/cm3 |
Viscosity 23℃,10S |
ISO3219 |
95000 mPa.s |
Component B |
|
|
Color |
|
Transparent |
Density 23℃ |
|
0.9 g/cm3 |
Viscosity 23℃,10S-1 |
ISO3219 |
1000 mPa.s |
Technical data(A/B mixed) |
|
|
Mix ratio(weight) |
A:B |
10:1 |
Viscosity 23℃,10S-1 |
ISO3219 |
80000 Pa.s |
Curing time |
|
See curing conditions |
Technical data(cured) |
125±2℃*200 S |
|
Color |
|
Transparent |
Density 23℃ |
ISO2781 |
1.07 g/cm3 |
Hardness |
DIN 53505 |
35 |
Tensile strength |
DIN 53504 |
5 Mpa |
Elongation at break |
DIN 53504 |
400% |
Tear strength |
ASTMD 624B |
15 KN/m |