Post cured free liquid silicone rubber with high bite force IOTA M6060K
Post cured free high bite force liquid silicone rubber IOTA M6040K
Post cured free liquid silicone rubber with high bite force IOTA M6050K
Post cured free liquid silicone rubber IOTA M6060
Post cured free liquid silicone rubber IOTA M6020 A/B
Description
IOTA M6060K A/B is post cured free liquid silicone rubber with high bite force.
Features
Two components, 1:1 mixture ratio
Excellent mold release
VOC is less than 0.5%
Rapid heat curing
Excellent mechanical properties
Meet the requirements of BfR、FDA and ROHS
Application
Baby care
Food contact
Sealing ring
Other injection products, etc.
Curing
Temperature |
Curing time,2mm thickness |
130℃ |
90 S |
150℃ |
45 S |
NOTES
IOTA M6060K A/B a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
2. Only same batch of components A and B could be mixed together.
3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.
Technical data
Properties |
Test method |
Value |
Uncured products |
||
Component A |
|
|
Color |
|
transparent |
Density (23℃) |
|
1.12 g/cm3 |
Viscosity (23℃,10S-1) |
ISO3219 |
350 Pa.s |
Component B |
|
|
Color |
|
transparent |
Density (23℃) |
|
1.12 g/cm3 |
Viscosity (23℃,10S-1 ) |
ISO3219 |
300 Pa.s |
Technical data(A/B mixed) |
|
|
Mixture ratio(weight) |
A:B |
1:1 |
Viscosity(23℃,10S-1) |
ISO3219 |
350 Pa.s |
Curing time |
|
See curing conditions |
Technical data(cured) |
(125±2℃,after vulcanizing 5min) |
|
Color |
|
transparent |
Density (23℃) |
ISO2781 |
1.12 g/cm3 |
Hardness |
DIN 53505 |
60 |
Tensile strength |
DIN 53504 |
9 Mpa |
Elongation |
DIN 53504 |
450% |
Tear strength |
ASTMD 624B |
38 KN/m |
Packaging & storage
A component 200 Kg/drum,B component 200 Kg/dum.
Store under 23℃ to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.