Description
M6040 A/B is a liquid silicone rubber free of post cured.
Features
Two-component, 1:1 mixing ratio
Excellent mold release
VOC less than 0.5%
Fast thermal curing
Excellent mechanical properties
Meet the requirements of BfR、FDA and ROHS
Applications
Baby care
Food contact
Sealing ring
Other injection products, etc.
Curing
Temperature |
Curing time, 2mm thickness |
130℃ |
90 S |
150℃ |
45 S |
IOTA M6040 A/B is a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
Only same batch of components A and B could be mixed together.
In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.
Technical data
Properties |
Test method |
Value |
Uncured products |
|
|
Component A |
|
|
Color |
|
Transparent |
Density 23℃ |
|
1.11 g/cm3 |
Viscosity 23℃, 10S-1 |
ISO3219 |
320 Pa.s |
Component B |
|
|
Color |
|
Transparent |
Density 23℃ |
|
1.11 g/cm3 |
Viscosity 23℃, 10S-1 |
ISO3219 |
280 Pa.s |
Product data (A+B mix) |
|
|
Mixing ratio (weight) |
A:B |
1:1 |
Viscosity 23℃, 10S-1 |
ISO3219 |
300 Pa.s |
Curing time |
|
See curing conditions |
Product data (after curing) |
(125±2℃, cured for 5min) |
|
Color |
|
Transparent |
Density 23℃ |
|
1.11 g/cm3 |
Hardness |
DIN 53505 |
40 |
Tensile Strength |
DIN 53504 |
8 MPa |
Elongation |
DIN 53504 |
580 % |
Tear strength |
ASTMD 624B |
30 KN/m |
Packaging & storage
A component 200 Kg/drum,B component 200 Kg/dum.
Store under 23℃ to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.