Description
IOTA M4335A/B is a low viscosity liquid silicone rubber with good adhesion to fabrics.
Advantages:
Two component, 10:1 mixing ratio
Excellent liquidity
Good adhesion to fabrics
Rapid heat curing
Excellent mechanical properties
Application:
Silk screen printing
Copper plate transfer printing
Silicone printing
Fingerprint printing, etc
Curing condition
|
Temperature |
Curing time, 1cm thickness |
|
125°C |
200s |
NOTES
1. IOTA M4335 A/B is a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
2. Only same batch of components A and B could be mixed together
3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.
Packing and storage
Component A: 20kg/drum, component B: 2kg/drum
Store at room temperature under 23 ℃ to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.
Technical index:
|
Properties |
Test method |
Value |
|
Uncured |
|
|
|
Component A |
|
|
|
Color |
|
Translucent |
|
Density 23℃ |
|
1.08 g/cm3 |
|
Viscosity 23℃，10S |
ISO3219 |
95000 mPa.s |
|
Component B |
|
|
|
Color |
|
Transparent |
|
Density 23℃ |
|
0.9 g/cm3 |
|
Viscosity 23℃，10S-1 |
ISO3219 |
1000 mPa.s |
|
Technical data（A/B mixed） |
|
|
|
Mix ratio（weight） |
A:B |
10:1 |
|
Viscosity 23℃，10S-1 |
ISO3219 |
80000 Pa.s |
|
Curing time |
|
See curing conditions |
|
Technical data（cured） |
125±2℃*200 S |
|
|
Color |
|
Transparent |
|
Density 23℃ |
ISO2781 |
1.07 g/cm3 |
|
Hardness |
DIN 53505 |
35 |
|
Tensile strength |
DIN 53504 |
5 Mpa |
|
Elongation at break |
DIN 53504 |
400% |
|
Tear strength |
ASTMD 624B |
15 KN/m |