Condensation type mold silicone rubber

    Condensation type mold silicone rubber

    100:2 two-component liquid silicone rubber belongs to condensation type mold silicone rubber.  When part A and B are mixed in 100:2 weight, the crosslinking reaction can occur, and the elastic body with certain hardness is formed after curing. It has many advantages, such as good fluidity, easy to operate with low viscosity. After curing, it has heat resistance, high temperature resistance, corrosion resistance, solvent resistance, high tensile and tear strength, low linear shrinkage, high turning model times. It is a cast of gypsum, cement, POLY-RESIN, PU, AB water, ABS material of the elastic mold material, it is widely used in the production and reproduction of sludge, toys, gifts, reliefs, statues, city sculpture, cement products, hand plate, car model, model of home appliances, mold products such as soap.

     

    Technical data:

    Model Numbe

    Appearance

    Hardness

    (A)    

    Viscosity

    (cps)

    Tear strength

    (KN/m)

    Tensile strength

    (Mpa)

    Elongation

    (%)

    Mixing time

    (Min)

    IOTA-800/900

    White/

    Semitransparent

    0±2

    800010000

    5±2

    2.03

    580±50

    1525

    IOTA-805/905

    White/

    Semitransparent

    5±2

    800010000

    8±2

    2.12

    550±50

    1525

    IOTA-810/910

    White/

    Semitransparent

    10±2

    800010000

    10±2

    2.46

    500±50

    1525

    IOTA-815/915

    White/

    Semitransparent

    15±2

    15000±2000

    15±2

    2.56

    450±50

    1525

    IOTA-820/920

    White/

    Semitransparent

    20±2

    20000±2000

    20±2

    2.57

    420±50

    1525

    IOTA-825/925

    White/

    Semitransparent

    25±2

    23000±2000

    23±2

    3.98

    400±50

    1525

    IOTA-830/930

    White/

    Semitransparent

    3035

    25000±2000

    22±2

    3.17

    300±50

    1525

    The above parameters are not the entire data and can be adjusted according to your requirements.

    Precautions For Use

    1. Before large-scale use, please do small amount of trial, familiar with the production skills to avoid errors.

    2. Do according to the manufacturer's instructions ratio for quantity, and the weighing accuracy, please remember that the ratio is by weight rather than volume. After the mixing of AB silicone rubber, stir it fully to avoid not cure or incomplete cure.

    3. If you want to speed up the curing time, you can heating up when liquid silicone rubber initially solidified, but could not heating up immediately after pouring which will cause non-curing because of the volatilization of curing agent. .

    4. When mixing the AB silicone, mixing in the same direction. When pour glue, take a little bit of the higher and same position on the female die on the same position, let the glue flow flat on the master die, it will increase the flow time of the glue to reduce the bubble. 

    Products Procedure
    1. According to the actual situation, the master module is put in the frame and fixed.

    2. Choose smooth material to make the mold frame, such as an acrylic plate.

    3. The silicone rubber and curing agent are mixed in 100:2 weight ratio and fully mixed evenly.

    4. Spray a little release agent in the female die and the die frame wall.

    5. Put the model frame into the vacuum machine according to the actual situation,. (optional).

    6. Vacuum exhaust bubble treatment.

    7. Pour the bubble in the mold into the mold box.

    8. Wait for stripping can be cured.


     